Significant reduction in processing time for Ca0.95Ce0.05MnO3 thermoelectric ceramics

Sotelo, A. (Universidad de Zaragoza) ; Amirkhizi, P. ; Dura, O.J. ; García, G. ; Asensio, A.C. ; Torres, M.A. (Universidad de Zaragoza) ; Madre, M.A. (Universidad de Zaragoza) ; Kovalevsky, A. ; Rasekh, Sh

Resumen: Attrition-milling process has been applied to Ce-doped CaMnO3 precursors to obtain small grain-size powders. The use of Ce4+ as dopant instead a Rare Earth3+ has allowed decreasing by 50% the atomic proportion of dopant, to obtain equivalent charge carrier concentration, which is required for attaining promising properties for thermoelectric applications. An impressive decrease in thermal processing time was achieved, together with an increase in thermoelectric performances, when compared to classically prepared materials. XRD and SEM analysis have confirmed that the final material is nearly single phase. Moreover, grain sizes and density increase with the sintering duration. These microstructural differences are reflected in a significant decrease in electrical resistivity, when compared to the samples prepared from ball-milled precursors (used as reference), without drastically modifying the Seebeck coefficient values. On the other hand, despite of their high electrical conductivity, thermal conductivity is decreased for short time sintered materials, leading to the highest ZT values at 800 °C (∼0.27) in samples sintered for 1 h at 1310 °C. These values are among the best reported in the literature, but they have been obtained in very short time using a simple, and easily scalable process. The suggested approach presented in this work appears particularly promising for large-scale production of oxide-based thermoelectric modules for power generation.

Idioma: Inglés

DOI: 10.1016/j.ceramint.2023.09.107

Año: 2023

Publicado en: Ceramics International 49, 23 Part A (2023), 37793-37799
ISSN: 0272-8842

Factor impacto JCR: 5.1 (2023)

Categ. JCR: MATERIALS SCIENCE, CERAMICS rank: 3 / 31 = 0.097 (2023) - Q1 - T1

Factor impacto CITESCORE: 9.4 - Ceramics and Composites (Q1) - Process Chemistry and Technology (Q1) - Materials Chemistry (Q1) - Electronic, Optical and Magnetic Materials (Q1) - Surfaces, Coatings and Films (Q1)

Factor impacto SCIMAGO: 0.938 - Electronic, Optical and Magnetic Materials (Q1) - Ceramics and Composites (Q1) - Surfaces, Coatings and Films (Q1) - Materials Chemistry (Q1) - Process Chemistry and Technology (Q2)

Financiación: info:eu-repo/grantAgreement/ES/DGA/T54-23R
Financiación: info:eu-repo/grantAgreement/ES/FEDER/UIDB/50011/2020
Financiación: info:eu-repo/grantAgreement/ES/FEDER/UIDP/50011/2020
Financiación: info:eu-repo/grantAgreement/ES/UZ/JIUZ-2022-IAR-09

Tipo y forma: Artículo (Versión definitiva)

Área (Departamento): Área Expresión Gráfica en Ing. (Dpto. Ingeniería Diseño Fabri.)
Área (Departamento): Área Cienc.Mater. Ingen.Metal. (Dpto. Ciencia Tecnol.Mater.Fl.)