Thermal Conductivity and Thermoelectric Power of Yb-Substituted Bi-2212 Superconductor
Resumen: In the present study, Bi2Sr2CaCu2-xYbxO8+y where x = 0.0, 0.05, 0.1 and 0.25, superconductor materials were textured using the Laser Floating Zone technique. After annealing the as-grown materials, they were characterized by thermal conductivity (¿-T), thermoelectric power (S-T), and electrical resistivity (R-T) measurements performed from room temperature down to 20 K. The thermoelectric power is positive in all cases and is found to increase with decreasing temperature, reaching the maximum value (peak) around the samples TC values and dropping rapidly to zero below TC. Electrical resistivity measurements show a slight decrease of TC when Yb substitution is raised. In spite of this effect, TC values are higher than 90 K in all cases. On the other hand, Yb substitution also decreases thermal conductivity, compared with the undoped samples.
Idioma: Inglés
DOI: 10.1088/1742-6596/667/1/012001
Año: 2016
Publicado en: Journal of Physics: Conference Series 667, 1 (2016), 012001 [6 p.]
ISSN: 1742-6588

Factor impacto SCIMAGO: 0.24 - Physics and Astronomy (miscellaneous) (Q3)

Tipo y forma: Artículo (Versión definitiva)
Área (Departamento): Área Cienc.Mater. Ingen.Metal. (Dpto. Ciencia Tecnol.Mater.Fl.)

Creative Commons Debe reconocer adecuadamente la autoría, proporcionar un enlace a la licencia e indicar si se han realizado cambios. Puede hacerlo de cualquier manera razonable, pero no de una manera que sugiera que tiene el apoyo del licenciador o lo recibe por el uso que hace.


Exportado de SIDERAL (2023-12-21-13:40:41)


Visitas y descargas

Este artículo se encuentra en las siguientes colecciones:
Artículos



 Registro creado el 2016-04-07, última modificación el 2023-12-21


Versión publicada:
 PDF
Valore este documento:

Rate this document:
1
2
3
 
(Sin ninguna reseña)