Laser machining and in vitro assessment of wollastonite-tricalcium phosphate eutectic glasses and glass-ceramics
Resumen: Bioactivity and ingrowth of ceramic implants is commonly enhanced by a suitable interconnected porous network. In this work, the laser machining of CaSiO3-Ca3(PO4)2 biocompatible eutectic glass-ceramics and glasses was studied. For this purpose, 300 µm diameter craters were machined by using pulsed laser radiation at 532 nm with a pulsewidth in the nanosecond range. Machined samples were soaked in simulated body fluid for 2 months to assess the formation of a hydroxyapatite layer on the surface of the laser machined areas. The samples were manufactured by the laser floating zone technique using a CO2 laser. Morphology, composition and microstructure of the machined samples were described by Field Emission Scanning Electron Microscopy, Energy Dispersive X-ray Spectroscopy and micro-Raman Spectroscopy.
Idioma: Inglés
DOI: 10.3390/ma11010125
Año: 2018
Publicado en: MATERIALS 11, 1 (2018), [10 pp]
ISSN: 1996-1944

Tipo y forma: Artículo (Versión definitiva)
Área (Departamento): Ciencia de los Materiales e Ingeniería Metalúrgica (Departamento de Ciencia y Tecnología de Materiales y Fluidos)

Creative Commons Debe reconocer adecuadamente la autoría, proporcionar un enlace a la licencia e indicar si se han realizado cambios. Puede hacerlo de cualquier manera razonable, pero no de una manera que sugiera que tiene el apoyo del licenciador o lo recibe por el uso que hace.


Exportado de SIDERAL (2018-02-12-10:48:33)

Este artículo se encuentra en las siguientes colecciones:
Artículos > Artículos por área > Ciencia de los Materiales e Ingeniería Metalúrgica



 Registro creado el 2018-02-12, última modificación el 2018-02-12


Versión publicada:
 PDF
Valore este documento:

Rate this document:
1
2
3
 
(Sin ninguna reseña)