Effect of Na-doping on thermoelectric and magnetic performances of textured Bi2Sr2Co2Oy ceramics
Resumen: Bi2Sr2-xNaxCo2Ox (x = 0.0, 0.025, 0.050, 0.075, 0.100, and 0.125) samples were prepared through the solid-state route and textured using the laser floating zone technique. Microstructural analysis of as-grown samples showed well oriented grains and a relatively high amount of secondary phases due to their incongruent melting. Annealing procedure has drastically decreased the number and amount of secondary phases. Moreover, Na-doping has further decreased the secondary phases content and improved grain alignment. These modifications have been reflected in a large decrease of electrical resistivity with the annealing procedure. The maximum power factor values have been obtained in 0.075 Na-doped annealed samples, 0.20 mW/K2m, which are much higher than the best values obtained in textured materials through hot uniaxial pressing. Magnetic properties were very similar for all samples, with paramagnetic Curie temperature and effective magnetic moment values of -48.6 K and ˜2 µB, respectively.
Idioma: Inglés
DOI: 10.1016/j.jeurceramsoc.2017.09.006
Año: 2018
Publicado en: JOURNAL OF THE EUROPEAN CERAMIC SOCIETY 38, 2 (2018), 515-520
ISSN: 0955-2219

Factor impacto JCR: 4.029 (2018)
Categ. JCR: MATERIALS SCIENCE, CERAMICS rank: 1 / 28 = 0.036 (2018) - Q1 - T1
Factor impacto SCIMAGO: 1.219 - Materials Chemistry (Q1) - Ceramics and Composites (Q1)

Financiación: info:eu-repo/grantAgreement/ES/DGA-FEDER/T12
Financiación: info:eu-repo/grantAgreement/ES/DGA-FEDER/T87
Financiación: info:eu-repo/grantAgreement/ES/MINECO-FEDER/MAT2013-46505-C3-1-R
Financiación: info:eu-repo/grantAgreement/ES/UZ/UZ2017-TEC-03
Tipo y forma: Article (PostPrint)
Área (Departamento): Área Expresión Gráfica en Ing. (Dpto. Ingeniería Diseño Fabri.)
Área (Departamento): Área Cienc.Mater. Ingen.Metal. (Dpto. Ciencia Tecnol.Mater.Fl.)


Rights Reserved All rights reserved by journal editor


Exportado de SIDERAL (2020-01-17-21:24:09)

Este artículo se encuentra en las siguientes colecciones:
Articles



 Record created 2019-03-15, last modified 2020-01-17


Postprint:
 PDF
Rate this document:

Rate this document:
1
2
3
 
(Not yet reviewed)