Elusive super-hard B6C accessible through the laser-floating zone method
Resumen: Boron carbide is among the most promising ceramic materials nowadays: their mechanical properties are outstanding, and they open potential critical applications in near future. Since sinterability is the most critical drawback to this goal, innovative and competitive sintering procedures are attractive research topics in the science and technology of this carbide. This work reports the pioneer use of the laser-floating zone technique with this carbide. Crystallographic, microstructural and mechanical characterization of the so-prepared samples is carefully analysed. One unexpected output is the fabrication of a B6C composite when critical conditions of growth rate are adopted. Since this is one of the hardest materials in Nature and it is achievable only under extremely high pressures and temperatures in hot-pressing, the use of this technique offers a promising alternative for the fabrication. Hardness and elastic modulus of this material reached to 52¿GPa and 600¿GPa respectively, which is close to theoretical predictions reported in literature.
Idioma: Inglés
DOI: 10.1038/s41598-019-49985-2
Año: 2019
Publicado en: SCIENTIFIC REPORTS 9, 1 (2019), 13340 [10 pp.]
ISSN: 2045-2322

Factor impacto SCIMAGO:

Tipo y forma: Artículo (Versión definitiva)
Área (Departamento): Área Cienc.Mater. Ingen.Metal. (Dpto. Ciencia Tecnol.Mater.Fl.)

Creative Commons Debe reconocer adecuadamente la autoría, proporcionar un enlace a la licencia e indicar si se han realizado cambios. Puede hacerlo de cualquier manera razonable, pero no de una manera que sugiera que tiene el apoyo del licenciador o lo recibe por el uso que hace.


Exportado de SIDERAL (2019-11-05-11:48:19)

Este artículo se encuentra en las siguientes colecciones:
Artículos



 Registro creado el 2019-11-05, última modificación el 2019-11-05


Versión publicada:
 PDF
Valore este documento:

Rate this document:
1
2
3
 
(Sin ninguna reseña)