Surface activation of calcium zirconate-calcium stabilized zirconia eutectic ceramics with bioactive wollastonite-tricalcium phosphate coatings

Sola, Daniel ; Chueca, Eloy ; Wang, Shunheng ; Peña, José Ignacio (Universidad de Zaragoza)

Resumen: In this work, we have developed and characterized a ceramic composite based on a core of directionally solidified calcium zirconate-calcium stabilized zirconia (CZO-CSZ) eutectic composite coated with a bioactive glass-ceramic. The aim is to research new orthopedic implants as an alternative to conventional 3Y-TZP bioinert ceramics. The CZO-CSZ eutectic rods were grown from the melt of rods of CaO-ZrO2 in the eutectic composition using the laser floating zone technique (LFZ). The mechanical results indicated that directional eutectics prepared with this technique exhibited good mechanical strength and significant hardness and toughness. The LFZ technique was also used to melt the bioactive coating previously placed by dip coating on the CZO-CSZ rod surface. Depending on the thickness of the coating and the applied laser power, an alloying or coating process was achieved. In the first case, the coating was diluted with the surface of the eutectic cylinder, leading to the segregation of the calcium zirconate and zirconia phases and the formation of a bioactive phase embedding zirconia particles. In the second case, a layer of ceramic glass was formed, well attached to the eutectic cylinder. These layers were both studied from the microstructural and bioactivity points of view.

Idioma: Inglés

DOI: 10.3390/jfb14100510

Año: 2023

Publicado en: Journal of Functional Biomaterials 14, 10 (2023), 510 [12 pp.]
ISSN: 2079-4983

Factor impacto JCR: 5.0 (2023)

Categ. JCR: ENGINEERING, BIOMEDICAL rank: 27 / 122 = 0.221 (2023) - Q1 - T1
Categ. JCR: MATERIALS SCIENCE, BIOMATERIALS rank: 18 / 53 = 0.34 (2023) - Q2 - T2

Factor impacto CITESCORE: 4.6 - Biomedical Engineering (Q2) - Biomaterials (Q3)

Factor impacto SCIMAGO: 0.722 - Biomedical Engineering (Q2) - Biomaterials (Q2)

Financiación: info:eu-repo/grantAgreement/ES/DGA/T02-20R

Tipo y forma: Artículo (Versión definitiva)

Área (Departamento): Área Cienc.Mater. Ingen.Metal. (Dpto. Ciencia Tecnol.Mater.Fl.)