Magnetic compensation in sputtered ferrimagnetic Mn 4-x Ga x N thin films
Resumen: Fully compensated ferrimagnets are attracting increasing attention for spintronics. Here we report a series of Mn 4−x Ga x N ferrimagnetic thin films grown on (100)-oriented MgO by magnetron sputtering. A small tetragonal distortion with c/a = 0.99 leads to perpendicular magnetic anisotropy with a [001] easy axis. The magnetisation decreases with increasing Ga content up to x = 0.18, where the magnetic moment is close to zero at room temperature. It increases with further increase of x, indicating the magnetic compensation composition has been crossed and the dominant sublattice has switched from Mn on the corner sites, where it is progressively replaced by nonmagnetic Ga, to noncollinear Mn on the face-centered sites. Compensation found at 235 K in a remanent scan of the x = 0.18 film is confirmed by measurements of the anomalous Hall effect and interpolation of the inverse coercivity. This work establishes the conditions for thin film growth of Mn 4−x Ga x N that could be used for room-temperature ferrimagnetic spintronics. The behaviour of thin films is compared with that of bulk material.
Idioma: Inglés
DOI: 10.1088/1361-6463/ad4a81
Año: 2024
Publicado en: JOURNAL OF PHYSICS D-APPLIED PHYSICS 57, 35 (2024), 355005 [9 pp.]
ISSN: 0022-3727

Tipo y forma: Artículo (Versión definitiva)

Creative Commons Debe reconocer adecuadamente la autoría, proporcionar un enlace a la licencia e indicar si se han realizado cambios. Puede hacerlo de cualquier manera razonable, pero no de una manera que sugiera que tiene el apoyo del licenciador o lo recibe por el uso que hace.


Exportado de SIDERAL (2024-09-20-13:01:48)


Visitas y descargas

Este artículo se encuentra en las siguientes colecciones:
Artículos



 Registro creado el 2024-09-20, última modificación el 2024-09-20


Versión publicada:
 PDF
Valore este documento:

Rate this document:
1
2
3
 
(Sin ninguna reseña)