000061452 245__ $$aEffect of Ag additions on the Bi1.6Pb0.4Sr2Co1.8Ox thermoelectric properties
000061452 260__ $$c2013
000061452 5060_ $$aAccess copy available to the general public$$fUnrestricted
000061452 5203_ $$aBi1.6Pb0.4Sr2Co1.8Ox thermoelectric ceramics with small Ag additions (0, 1, and 3 wt.%) have been successfully produced by a sol-gel method via nitrates. Microstructure has shown a reduction on the amount of secondary phases and an increase on the bulk density with increasing Ag contents. The microstructural evolution, as a function of Ag content, is confirmed with the electrical resistivity values which show an important decrease for the 3 wt.% Ag samples, leading to maximum power factor values  of  about  0.025  mW/K2.m  at  room  temperature,  which  is  about  two  times  higher  than  the  obtained  for  the  Ag-free sintered samples.   

Se  han  preparado  cerámicas  termoeléctricas  de  composición  Bi1.6Pb0.4Sr2Co1.8Ox  con  pequeñas  adiciones  de  Ag  (0,  1,  y  3  % en peso) por medio de un método sol-gel a partir de los nitratos metálicos. La microestructura ha mostrado una reducción de la cantidad de fases secundarias y un aumento de la densidad del material al aumentar la cantidad de Ag. La evolución microestructural, en función del contenido de Ag, se ha confirmado con los valores de la resistividad eléctrica que muestra una reducción importante para las muestras con 3 % en peso de Ag, lo que lleva a alcanzar valores máximos del factor de potencia de alrededor de 0.025 mW/K2.m a temperatura ambiente, que es dos veces mayor que el obtenido para muestras sinterizadas sin Ag
000061452 536__ $$9info:eu-repo/grantAgreement/ES/CSIC/JAE-PreDoc2010$$9info:eu-repo/grantAgreement/ES/DGA/T12$$9info:eu-repo/grantAgreement/ES/DGA/T87$$9info:eu-repo/grantAgreement/ES/MICINN/MAT2008-00429$$9info:eu-repo/grantAgreement/ES/UZ/UZ2011-TEC-03
000061452 540__ $$9info:eu-repo/semantics/openAccess$$aby-nc$$uhttp://creativecommons.org/licenses/by-nc/3.0/es/
000061452 590__ $$a0.343$$b2013
000061452 591__ $$aMATERIALS SCIENCE, CERAMICS$$b20 / 25 = 0.8$$c2013$$dQ4$$eT3
000061452 655_4 $$ainfo:eu-repo/semantics/article$$vinfo:eu-repo/semantics/publishedVersion
000061452 700__ $$aRasekh, Sh.
000061452 700__ $$aConstantinescu, G.
000061452 700__ $$0(orcid)0000-0003-3995-5763$$aTorres, M.A.$$uUniversidad de Zaragoza
000061452 700__ $$aMadre, M.A.
000061452 700__ $$aSotelo, A.
000061452 7102_ $$15002$$2305$$aUniversidad de Zaragoza$$bDepartamento de Ingeniería de Diseño y Fabricación$$cExpresión Gráfica de la Ingeniería
000061452 773__ $$g52, 2 (2013), 93-97$$pBol. Soc. Esp. Ceram. Vidr.$$tBOLETIN DE LA SOCIEDAD ESPAÑOLA DE CERAMICA Y VIDRIO$$x0366-3175
000061452 8564_ $$s2456171$$uhttps://zaguan.unizar.es/record/61452/files/texto_completo.pdf$$yVersión publicada
000061452 8564_ $$s112476$$uhttps://zaguan.unizar.es/record/61452/files/texto_completo.jpg?subformat=icon$$xicon$$yVersión publicada
000061452 909CO $$ooai:zaguan.unizar.es:61452$$particulos$$pdriver
000061452 951__ $$a2017-06-12-09:14:14
000061452 980__ $$aARTICLE