75370 20191122145056.0 doi 10.1016/j.solmat.2017.09.031 sideral 101852 ART-2018-101852 eng (orcid)0000-0003-3480-398X Oliete, P. B. Universidad de Zaragoza Selective thermal emission of directionally solidified Al2O3/Y3-xErxAl5O12 eutectics: influence of the microstructure, temperature and erbium content 2018 Access copy available to the general public Unrestricted Directionally solidified eutectic rods of Al2O3-Y3-xErxAl5O12 (0 = x = 3) composition have been grown using the laser floating zone method at processing rates of 25 mm/h and 750 mm/h. For all the samples the microstructure presents the same morphology, consisting of an interpenetrated 3D eutectic network of both Al2O3 and garnet phases, while eutectic interspacing strongly depends on the solidification rate. Optical absorption, luminescence and thermal emission have been investigated as a function of the growth rate and the erbium content. From the luminescence characterization it can be concluded that erbium ions are present in the eutectic only in the garnet phase. Near infrared thermal emission has been measured at temperatures ranging from 1000 to 1500 °C. Selective emission consisting of an emission band at 1540 nm and a weaker line at 970 nm, ascribed to the radiative de-excitation of the thermally excited Er3+ ions from the 4I13/2 and 4I11/2 multiplets to the 4I15/2 ground state respectively, has been detected in all the samples containing erbium. The influence of the erbium content, the microstructure and the temperature on the thermal emission has been investigated. The strongest selective emission has been obtained for samples with x=3 although it does not increase proportionally to the erbium content. The thermal emission becomes more intense when the temperature is increased but the selective emission seems to saturate at temperatures higher than 1300 °C. This effect is especially noticeable for x=3 and is attributed to thermally activated non-radiative de-excitation channels. It is suggested that these channels become effective through energy transfer among Er3+ ions and towards killers. info:eu-repo/grantAgreement/ES/MINECO/MAT2013-41045-R info:eu-repo/grantAgreement/ES/MINECO/MAT2016-77769-R info:eu-repo/semantics/openAccess by-nc-nd http://creativecommons.org/licenses/by-nc-nd/3.0/es/ 6.019 2018 ENERGY & FUELS 14 / 103 = 0.136 2018 Q1 T1 PHYSICS, APPLIED 22 / 148 = 0.149 2018 Q1 T1 MATERIALS SCIENCE, MULTIDISCIPLINARY 48 / 293 = 0.164 2018 Q1 T1 1.62 2018 Electronic, Optical and Magnetic Materials 2018 Q1 Surfaces, Coatings and Films 2018 Q1 Renewable Energy, Sustainability and the Environment 2018 Q1 info:eu-repo/semantics/article info:eu-repo/semantics/acceptedVersion (orcid)0000-0001-8751-0983 Orera, A. Universidad de Zaragoza (orcid)0000-0002-5793-2058 Sanjuán, M. L. Universidad de Zaragoza (orcid)0000-0003-0747-405X Merino, R. I. Universidad de Zaragoza 5001 065 Universidad de Zaragoza Dpto. Ciencia Tecnol.Mater.Fl. Área Cienc.Mater. Ingen.Metal. 2003 395 Universidad de Zaragoza Dpto. Física Materia Condensa. Área Física Materia Condensada 174 (2018), 460-468 Sol. energy mater. sol. cells SOLAR ENERGY MATERIALS AND SOLAR CELLS 0927-0248 956255 http://zaguan.unizar.es/record/75370/files/texto_completo.pdf Postprint 54378 http://zaguan.unizar.es/record/75370/files/texto_completo.jpg?subformat=icon icon Postprint oai:zaguan.unizar.es:75370 articulos driver 2019-11-22-14:46:17 ARTICLE