Oliete, P. B. (Universidad de Zaragoza) ; Mesa, M. C. ; Merino, R. I. (Universidad de Zaragoza) ; Orera, V. M. (Universidad de Zaragoza)

Resumen: Al2O3-Yb3Al5O12 eutectic rods were directionally solidified using the laser floating zone method at rates between 25 and 750 mm/h. The microstructure consisted of an interpenetrated network of both eutectic phases for all the growth rates. The size of the phases was strongly dependent on the growth rate, the eutectic interspacing decreasing from 4.5 µm at the lowest growth rate to 600 nm at 750 mm/h. The optical transmission of the sample with coarser microstructure was measured and compared with that of an Yb3Al5O12 single crystal grown "ad hoc" using the same method. The apparent "oscillator strength" of the single 2F7/2¿2F5/2 Yb3+ absorption band was larger in the eutectic sample than in the single crystal, which was attributed to the increase in the light path caused by multiple refractions at the eutectic interphases. The thermal emission of the eutectic rod was studied between 1000 °C and 1500 °C. An intense and relatively narrow emission band at about 1 µm corresponding to the 2F5/2¿2F7/2 Yb3+ electronic transition was observed in the whole temperature range. The intensity of the band increased with the temperature up to about 1300 °C. At higher temperatures a saturation of the selective emission was observed which was attributed to the competition between the increase in the thermal population of the excited state and the enhancement of the non-radiative de-excitation channels with the temperature.

Idioma: Inglés

DOI: 10.1016/j.solmat.2015.09.053

Año: 2016

Publicado en: SOLAR ENERGY MATERIALS AND SOLAR CELLS 144 (2016), 405-410
ISSN: 0927-0248

Factor impacto JCR: 4.784 (2016)

Categ. JCR: ENERGY & FUELS rank: 13 / 92 = 0.141 (2016) - Q1 - T1
Categ. JCR: PHYSICS, APPLIED rank: 22 / 147 = 0.15 (2016) - Q1 - T1
Categ. JCR: MATERIALS SCIENCE, MULTIDISCIPLINARY rank: 40 / 275 = 0.145 (2016) - Q1 - T1

Factor impacto SCIMAGO: 1.599 - Electronic, Optical and Magnetic Materials (Q1) - Surfaces, Coatings and Films (Q1) - Renewable Energy, Sustainability and the Environment (Q1)

Financiación: info:eu-repo/grantAgreement/ES/MINECO/MAT2013-41045-R
Financiación: info:eu-repo/grantAgreement/ES/UZ/CUD2014-TEC-11

Tipo y forma: Article (PostPrint)

Área (Departamento): Área Cienc.Mater. Ingen.Metal. (Dpto. Ciencia Tecnol.Mater.Fl.)
Área (Departamento): Área Física Materia Condensada (Dpto. Física Materia Condensa.)