Improvement of thermoelectric properties of Bi2Sr2Co1.8Ox through solution synthetic methods
Torres, M.A. (Universidad de Zaragoza) ; Sotelo, A. (Universidad de Zaragoza) ; Rasekh, Sh. ; Serrano, I. ; Constantinescu, G. ; Madre, M.A. (Universidad de Zaragoza) ; Diez, J.C. (Universidad de Zaragoza)
Resumen: Several solution synthetic methods, sol-gel and a polymeric route, have been studied in order to obtain Bi2Sr2Co1.8Ox ceramics with improved thermoelectric properties, compared to the classical solid state reaction. The products obtained by these
different methods have been compared using DTA-TGA, powder X-ray diffraction, scanning electron microscopy, and thermoelectric characterizations. All the samples obtained by solution synthesis show higher homogeneity and lower content of secondary phases. The main differences in thermoelectrical properties are due to the decrease of electrical resistivity in samples obtained by solution methods, compared with the solid state obtained samples. Between them, the decrease is especially high for those samples prepared by the polymer solution method. Therefore, the polymeric solution synthesis route is shown to yield a power factor four times higher than the obtained for the solid state and sol-gel methods at room temperature.
Idioma: Múltiples idiomas
Año: 2012
Publicado en: Boletin de la Sociedad Espanola de Ceramica y Vidrio 51, 1 (2012), 1-6
ISSN: 0366-3175
Factor impacto JCR: 0.404 (2012)
Categ. JCR: MATERIALS SCIENCE, CERAMICS rank: 16 / 27 = 0.593 (2012) - Q3 - T2
Financiación: info:eu-repo/grantAgreement/ES/DGA/T12
Financiación: info:eu-repo/grantAgreement/ES/DGA/T87
Financiación: info:eu-repo/grantAgreement/ES/MICINN/MAT2008-00429
Tipo y forma: Artículo (Versión definitiva)
Área (Departamento): Área Expresión Gráfica en Ing. (Dpto. Ingeniería Diseño Fabri.)
Área (Departamento): Área Cienc.Mater. Ingen.Metal. (Dpto. Ciencia Tecnol.Mater.Fl.)
Debe reconocer adecuadamente la autoría, proporcionar un enlace a la licencia e indicar si se han realizado cambios. Puede hacerlo de cualquier manera razonable, pero no de una manera que sugiera que tiene el apoyo del licenciador o lo recibe por el uso que hace. No puede utilizar el material para una finalidad comercial. Si remezcla, transforma o crea a partir del material, no puede difundir el material modificado.
Exportado de SIDERAL (2026-01-27-15:01:09)
Visitas y descargas
different methods have been compared using DTA-TGA, powder X-ray diffraction, scanning electron microscopy, and thermoelectric characterizations. All the samples obtained by solution synthesis show higher homogeneity and lower content of secondary phases. The main differences in thermoelectrical properties are due to the decrease of electrical resistivity in samples obtained by solution methods, compared with the solid state obtained samples. Between them, the decrease is especially high for those samples prepared by the polymer solution method. Therefore, the polymeric solution synthesis route is shown to yield a power factor four times higher than the obtained for the solid state and sol-gel methods at room temperature.
Idioma: Múltiples idiomas
Año: 2012
Publicado en: Boletin de la Sociedad Espanola de Ceramica y Vidrio 51, 1 (2012), 1-6
ISSN: 0366-3175
Factor impacto JCR: 0.404 (2012)
Categ. JCR: MATERIALS SCIENCE, CERAMICS rank: 16 / 27 = 0.593 (2012) - Q3 - T2
Financiación: info:eu-repo/grantAgreement/ES/DGA/T12
Financiación: info:eu-repo/grantAgreement/ES/DGA/T87
Financiación: info:eu-repo/grantAgreement/ES/MICINN/MAT2008-00429
Tipo y forma: Artículo (Versión definitiva)
Área (Departamento): Área Expresión Gráfica en Ing. (Dpto. Ingeniería Diseño Fabri.)
Área (Departamento): Área Cienc.Mater. Ingen.Metal. (Dpto. Ciencia Tecnol.Mater.Fl.)
Debe reconocer adecuadamente la autoría, proporcionar un enlace a la licencia e indicar si se han realizado cambios. Puede hacerlo de cualquier manera razonable, pero no de una manera que sugiera que tiene el apoyo del licenciador o lo recibe por el uso que hace. No puede utilizar el material para una finalidad comercial. Si remezcla, transforma o crea a partir del material, no puede difundir el material modificado.Exportado de SIDERAL (2026-01-27-15:01:09)
Enlace permanente:
Visitas y descargas
Este artículo se encuentra en las siguientes colecciones:
Artículos > Artículos por área > Ciencia de los Materiales e Ingeniería Metalúrgica
Artículos > Artículos por área > Expresión Gráfica de la Ingeniería
Registro creado el 2026-01-27, última modificación el 2026-01-27