Amine-functionalized mesoporous silica: A material capable of CO2 adsorption and fast regeneration by microwave heating
Resumen: The surface of ordered mesoporous (MCM-48) silica has been subjected to covalent grafting with silane molecules containing one to three amino groups. The dielectric properties of the materials were studied in detail, and the functionalized materials were used for CO2 adsorption at room temperature, followed by regeneration under either conventional heating or microwave irradiation. It has been found that, as the intensity of functionalization with amino groups increases (from mono- to tri-amino silanes) both the CO2 load and the dielectric response at microwave frequencies increase. In particular, functionalization with a tri-amino silane derivative gave the highest CO2 adsorption and the fastest microwave heating, resulting in a fourfold acceleration of adsorbent regeneration. The grafted material was fully stable for at least 20 adsorption-regeneration cycles, making it an ideal candidate for microwave-swing adsorption (MWSA) processes.
Idioma: Inglés
DOI: 10.1002/aic.15118
Año: 2016
Publicado en: AICHE JOURNAL 62, 2 (2016), 547-555
ISSN: 0001-1541

Factor impacto JCR: 2.836 (2016)
Categ. JCR: ENGINEERING, CHEMICAL rank: 35 / 135 = 0.259 (2016) - Q2 - T1
Factor impacto SCIMAGO: 1.034 - Biotechnology (Q1) - Environmental Engineering (Q1) - Chemical Engineering (miscellaneous) (Q1)

Financiación: info:eu-repo/grantAgreement/EUR/ERC/HECTOR-267626
Financiación: info:eu-repo/grantAgreement/ES/MEC/FPU12/06864
Tipo y forma: Artículo (PostPrint)
Área (Departamento): Área Ingeniería Química (Dpto. Ing.Quím.Tecnol.Med.Amb.)

Creative Commons Debe reconocer adecuadamente la autoría, proporcionar un enlace a la licencia e indicar si se han realizado cambios. Puede hacerlo de cualquier manera razonable, pero no de una manera que sugiera que tiene el apoyo del licenciador o lo recibe por el uso que hace. No puede utilizar el material para una finalidad comercial.


Exportado de SIDERAL (2020-02-21-13:24:45)

Este artículo se encuentra en las siguientes colecciones:
Artículos



 Registro creado el 2017-01-23, última modificación el 2020-02-21


Postprint:
 PDF
Valore este documento:

Rate this document:
1
2
3
 
(Sin ninguna reseña)