Improvement of thermoelectric properties of Ca0.9Gd0.1MnO3 by powder engineering through K2CO3 additions

Ferreira, N.M. ; Ferro, M.C. ; Sarabando, A.R. ; Ribeiro, A. ; Davarpanah, A. ; Amaral, V. ; Madre, M.A. (Universidad de Zaragoza) ; Kovalevsky, A.V. ; Torres, M.A. (Universidad de Zaragoza) ; Costa, F.M. ; Sotelo, A. (Universidad de Zaragoza)

Resumen: Oxide materials based on calcium manganite show clear prospects as thermoelectrics, provided by their stability at high temperatures and inherent flexibility in tuning the relevant electrical and thermal transport properties. Donor-doped CaMnO3 is an n-type semiconductor with a perovskite structure and relatively high thermoelectric performance. In this work, the precursor powders have been modified through potassium carbonate additions to produce Ca0.9Gd0.1MnO3 pellets without the usual delamination problems occurring during the compaction process. In order to demonstrate the relevant effects, several samples with different amounts of potassium carbonate (0–15 wt%) have been prepared. The results showed that potassium additions significantly facilitate the compaction procedure, while also improving the thermoelectric performances. The results also highlight the importance of porosity control for improving ZT, by decreasing the thermal conductivity without reduction of the electrical performance. The highest ZT values were observed for the samples processed at 15 wt% of potassium carbonate addition, exhibiting an improvement at least 30% at 800 °C when compared to the pure samples.

Idioma: Inglés

DOI: 10.1007/s10853-018-3058-x

Año: 2019

Publicado en: JOURNAL OF MATERIALS SCIENCE 54, 4 (2019), 3252-3261
ISSN: 0022-2461

Factor impacto JCR: 3.553 (2019)

Categ. JCR: MATERIALS SCIENCE, MULTIDISCIPLINARY rank: 108 / 314 = 0.344 (2019) - Q2 - T2

Factor impacto SCIMAGO: 0.798 - Materials Science (miscellaneous) (Q1) - Mechanics of Materials (Q1) - Mechanical Engineering (Q1)

Financiación: info:eu-repo/grantAgreement/ES/DGA/T54-17R
Financiación: info:eu-repo/grantAgreement/ES/MINECO-FEDER/MAT2017-82183-C3-1-R

Tipo y forma: Artículo (PostPrint)

Área (Departamento): Área Expresión Gráfica en Ing. (Dpto. Ingeniería Diseño Fabri.)
Área (Departamento): Área Cienc.Mater. Ingen.Metal. (Dpto. Ciencia Tecnol.Mater.Fl.)