Phase relations in the Nd2O3-Fe2O3 system: Structure and magnetic properties of perovskite NdFeO3 ceramics

Chudinovych, Olga V. ; Vedel, Dmytro V. ; Stasyuk, Oleksandr O. ; Samelyuk, Anatoly V. ; Aguirre, Myriam H. (Universidad de Zaragoza)

Resumen: The phase relations in the Nd2O3-Fe2O3 system at 1300 and 1400 degrees C were studied in the whole concentration range by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The isothermal cross-sections of the Nd2O3-Fe2O3 phase diagram at 1300 and 1400 degrees C are characterized by the presence of three single-phase (A-Nd2O3, NdFeO3, Fe2O3) and two two-phase (A-Nd2O3 + NdFeO3, NdFeO3 + Fe2O3) regions. The composition corresponding to the perovskite phase is 51 mol% Nd2O3 - 49 mol% Fe2O3. In the next step, the investigation was focused on this composition. Nanocrystalline NdFeO3 powders with perovskite structure were obtained by the Pechini method and heterogeneous precipitation from nitrate solutions. The influence of the production method on the microstructure, morphology and magnetic properties of the NdFeO3 nanopowders was studied. According to XRD, SEM and TEM, the synthesized perovskite NdFeO3 is single-phase with a particle size of 60-90 nm. The morphology of powder particles primarily depends on the synthesis method. The powder showed ferromagnetic behaviour and had saturation magnetization 0.8 and 0.81 emu/g.

Idioma: Inglés

DOI: 10.2298/PAC2403314C

Año: 2024

Publicado en: Processing and Application of Ceramics 18, 30 (2024), 314-322
ISSN: 1820-6131

Financiación: info:eu-repo/grantAgreement/EC/H2020/872631 /EU/Memristive and multiferroic materials for emergent logic units in nanoelectronics/MELON

Tipo y forma: Artículo (Versión definitiva)

Área (Departamento): Área Física Materia Condensada (Dpto. Física Materia Condensa.)