Influence of Ca substitution by Mg on the Ca3Co 4O9 performances
Constantinescu, G. ; Rasekh, S.H. ; Torres, M.A. (Universidad de Zaragoza) ; Chocarro, C. ; Díez, J.C. (Universidad de Zaragoza) ; Madre, M.A. (Universidad de Zaragoza) ; Sotelo, A. (Universidad de Zaragoza)
Resumen: Ca3-x Mgx Co4 O 9 polycrystalline thermoelectric ceramics with small amounts of Mg have been synthesized by the classical solid state method. Microstructural characterizations have shown that all the Mg has been incorporated into the Ca 3 Co4 O 9
structure and no Mg-based secondary phases have been identified. Apparent density measurements have shown that samples do not modify their density until 0.05 Mg content, decreasing for higher contents. Electrical resistivity decreases and Seebeck coefficient slightly raises when Mg content increases until 0.05 Mg addition. The improvement in both parameters leads to higher power factor values than the usually obtained in samples prepared by the conventional solid state routes and
close to those obtained in textured materials.
Idioma: Múltiples idiomas
Año: 2014
Publicado en: Boletin de la Sociedad Espanola de Ceramica y Vidrio 53, 1 (2014), 41-47
ISSN: 0366-3175
Factor impacto JCR: 0.29 (2014)
Categ. JCR: MATERIALS SCIENCE, CERAMICS rank: 22 / 26 = 0.846 (2014) - Q4 - T3
Financiación: info:eu-repo/grantAgreement/ES/DGA/T12
Financiación: info:eu-repo/grantAgreement/ES/DGA/T87
Tipo y forma: Artículo (Versión definitiva)
Área (Departamento): Área Expresión Gráfica en Ing. (Dpto. Ingeniería Diseño Fabri.)
Área (Departamento): Área Cienc.Mater. Ingen.Metal. (Dpto. Ciencia Tecnol.Mater.Fl.)
Debe reconocer adecuadamente la autoría, proporcionar un enlace a la licencia e indicar si se han realizado cambios. Puede hacerlo de cualquier manera razonable, pero no de una manera que sugiera que tiene el apoyo del licenciador o lo recibe por el uso que hace. No puede utilizar el material para una finalidad comercial. Si remezcla, transforma o crea a partir del material, no puede difundir el material modificado.
Exportado de SIDERAL (2026-01-27-15:01:37)
Visitas y descargas
structure and no Mg-based secondary phases have been identified. Apparent density measurements have shown that samples do not modify their density until 0.05 Mg content, decreasing for higher contents. Electrical resistivity decreases and Seebeck coefficient slightly raises when Mg content increases until 0.05 Mg addition. The improvement in both parameters leads to higher power factor values than the usually obtained in samples prepared by the conventional solid state routes and
close to those obtained in textured materials.
Idioma: Múltiples idiomas
Año: 2014
Publicado en: Boletin de la Sociedad Espanola de Ceramica y Vidrio 53, 1 (2014), 41-47
ISSN: 0366-3175
Factor impacto JCR: 0.29 (2014)
Categ. JCR: MATERIALS SCIENCE, CERAMICS rank: 22 / 26 = 0.846 (2014) - Q4 - T3
Financiación: info:eu-repo/grantAgreement/ES/DGA/T12
Financiación: info:eu-repo/grantAgreement/ES/DGA/T87
Tipo y forma: Artículo (Versión definitiva)
Área (Departamento): Área Expresión Gráfica en Ing. (Dpto. Ingeniería Diseño Fabri.)
Área (Departamento): Área Cienc.Mater. Ingen.Metal. (Dpto. Ciencia Tecnol.Mater.Fl.)
Debe reconocer adecuadamente la autoría, proporcionar un enlace a la licencia e indicar si se han realizado cambios. Puede hacerlo de cualquier manera razonable, pero no de una manera que sugiera que tiene el apoyo del licenciador o lo recibe por el uso que hace. No puede utilizar el material para una finalidad comercial. Si remezcla, transforma o crea a partir del material, no puede difundir el material modificado.Exportado de SIDERAL (2026-01-27-15:01:37)
Enlace permanente:
Visitas y descargas
Este artículo se encuentra en las siguientes colecciones:
Artículos > Artículos por área > Ciencia de los Materiales e Ingeniería Metalúrgica
Artículos > Artículos por área > Expresión Gráfica de la Ingeniería
Registro creado el 2026-01-27, última modificación el 2026-01-27