Effect of extrusion on the mechanical and rheological properties of a reinforced poly(lactic acid): Reprocessing and recycling of biobased materials
Resumen: The aim of this research paper is to study the behaviour of a common used biopolymer (Poly(Lactic Acid) (PLA)) after several reprocesses and how two different types of additives (a melt strength enhancer and a nanoadditive) affect its mechanical and rheological properties. Systematic extraction of extrudate samples from a twin-screw compounder was done in order to study the effect in the properties of the reprocessed material. Detailed rheological tests on a capillary rheometer as well as mechanical studies on a universal tensile machine after preparation of injected specimens were carried out. Results evidenced that PLA and reinforced PLA materials can be reprocessed and recycled without a remarkable loss in their mechanical properties. Several processing restrictions and specific phenomena were identified and are explained in the present manuscript.
Idioma: Inglés
DOI: 10.3390/ma8105360
Año: 2015
Publicado en: MATERIALS 8, 10 (2015), 7106-7117
ISSN: 1996-1944

Factor impacto JCR: 2.728 (2015)
Categ. JCR: MATERIALS SCIENCE, MULTIDISCIPLINARY rank: 63 / 271 = 0.232 (2015) - Q1 - T1
Factor impacto SCIMAGO: 0.83 - Materials Science (miscellaneous) (Q1)

Financiación: info:eu-repo/grantAgreement/ES/MINECO/PTQ-12-05223
Tipo y forma: Artículo (Versión definitiva)
Área (Departamento): Química Analítica (Departamento de Química Analítica)

Creative Commons Debe reconocer adecuadamente la autoría, proporcionar un enlace a la licencia e indicar si se han realizado cambios. Puede hacerlo de cualquier manera razonable, pero no de una manera que sugiera que tiene el apoyo del licenciador o lo recibe por el uso que hace.


Exportado de SIDERAL (2021-01-21-10:45:18)

Este artículo se encuentra en las siguientes colecciones:
Artículos > Artículos por área > Química Analítica



 Registro creado el 2015-12-16, última modificación el 2021-01-21


Versión publicada:
 PDF
Valore este documento:

Rate this document:
1
2
3
 
(Sin ninguna reseña)